First Nitroxide-Mediated Controlled Free-Radical Polymerization of Acrylic Acid

Abstract

Controlled poly(acrylic acid) homopolymers were synthesized for the first time by direct nitroxide-mediated polymerization of acrylic acid. The polymerizations were performed in 1,4-dioxane solution at 120 °C, using an alkoxyamine initiator based on the N - tert -butyl- N -(1-diethyl phosphono-2,2-dimethyl propyl) nitroxide, SG1. The kinetics were controlled by the addition of free nitroxide at the beginning of the polymerization and the optimal amount was 9 mol % with respect to the initiator. In this case, whatever the initiator concentration, all polymerizations exhibited the same rate and conversion reached 85−90% within 5 h. Although the rate constant of propagation of acrylic acid is very large, its reactivity is moderated by a low activation−deactivation equilibrium constant between active macroradicals and SG1-capped dormant chains. Various alkoxyamine concentrations were investigated to target different molar masses. At high initiator concentrations, the number-average molar mass, M n, increased linearly with monomer conversion and followed the theoretical values; the polydispersity indexes ranged between 1.3 and 1.5. At low initiator concentration (high target M n ), a deviation from linearity was observed in the M n vs conversion plot and was clearly assigned to chain transfer to 1,4-dioxane. From these results, the best experimental conditions to obtain well-defined homopolymers with the minimum amount of dead chains were identified.